Seamless carbon steel pipe ASTM A192 specification parameter table

Seamless carbon steel pipe ASTM A192 specification parameter table

ASTM A192 Carbon Steel Tube Specification covers seamless carbon steel boiler tubes for high pressure applications.
ASTM A192 seamless steel pipes are used as minimum wall thickness, seamless carbon steel boiler and superheater tubes for high pressure. CSC STEEL provides ASTM A192 steel pipes in hot-rolled and cold-drawn delivery conditions, usually used in high-pressure boilers (working pressure does not exceed 9.8Mpa , the working temperature is between 450â„ƒ-650â„ƒ) heating surface pipes, headers, economizers, superheaters, and reheaters.

ASTM 192 Seamless Steel TubeÂ Chemical Composition:

ASTM A192 Carbon Steel Chemical Composition C Mn Pâ‰¤ Sâ‰¤ Siâ‰¤

0.06-0.18 0.27-0.63 0.035 0.035 0.25

Â ASTM 192 Seamless Steel TubeÂ Mechanical Property:

Yield Strength (Mpa) Tensile Strength (Mpa) Elongation (%) Brinell Hardness Number
(WTâ‰¥)0.200In(5.1mm) Rockwell Hardness Number
(WT)0.200In(5.1mm)

â‰¥180 â‰¥325 â‰¥35 137HRB 77HRB

ASTM 192 Seamless Steel TubeÂ Outside diameter & tolerance:

Hot rolled Outside Diameter, mm Tolerance, mm

ODâ‰¤101.6 +0.4/-0.8

101.6ï¼œODâ‰¤177.8 +0.4/-1.2

Cold Drawn Outside Diameter, mm Tolerance, mm

ODï¼œ25.4 Â±0.10

25.4â‰¤ODâ‰¤38.1 Â±0.15

38.1ï¼œODï¼œ50.8 Â±0.20

50.8â‰¤ODï¼œ63.5 Â±0.25

63.5â‰¤ODï¼œ76.2 Â±0.30

76.2â‰¤ODâ‰¤101.6 Â±0.38

101.6ï¼œODâ‰¤177.8 +0.38/-0.64

Â ASTM 192 Seamless Steel TubeÂ Wall thickness & tolerance:

Hot rolled

Â Outside Diameter, mm Tolerance, %

ODâ‰¤101.6, WTâ‰¤2.4 +40/-0

ODâ‰¤101.6, 2.4ï¼œWTâ‰¤3.8 +35/-0

ODâ‰¤101.6, 3.8ï¼œWTâ‰¤4.6 +33/-0

ODâ‰¤101.6, WT>4.6 +28/-0

OD>101.6, 2.4ï¼œWTâ‰¤3.8 +35/-0

OD>101.6, 3.8ï¼œWTâ‰¤4.6 +33/-0

OD>101.6, WT>4.6 +28/-0

Cold Drawn
Â Outside Diameter, mm Tolerance, %

ODâ‰¤38.1 +20/-0

OD>38.1 +22/-0

ASTM 192 Seamless Steel TubeÂ Dimensions:

OD (mm) Wall Thickness(mm)

Â 2 2.5 3 3.5 4 4.5 5 6 6.5-7 7.5-8 8.5-9 9.5-10 11 12

Î¦25-Î¦28 â— â— â— â— â— â— Â Â Â Â Â Â Â Â

Î¦32 Â â— â— â— â— â— â— Â Â Â Â Â Â Â

Î¦34-Î¦36 Â â— â— â— â— â— â— Â Â Â Â Â Â Â

Î¦38 Â â— â— â— â— â— â— Â Â Â Â Â Â Â

Î¦40 Â Â â— â— â— â— â— Â Â Â Â Â Â Â

Î¦42 Â Â â— â— â— â— â— Â Â Â Â Â Â Â

Î¦45 Â Â â— â— â— â— â— â— Â Â Â Â Â Â

Î¦48-Î¦60 Â Â â— â— â— â— â— â— â— Â Â Â Â Â

Î¦63.5 Â Â Â â— â— â— â— â— â— â— Â Â Â Â

Î¦68-Î¦73 Â Â Â Â â— â— â— â— â— â— Â Â Â Â

Î¦76 Â Â Â Â â— â— â— â— â— â— â— â— â— â—

Î¦80 Â Â Â Â â— â— â— â— â— â— â— â— â— â—

Î¦83 Â Â Â Â â— â— â— â— â— â— â— â— â— â—

Î¦89 Â Â Â Â â— â— â— â— â— â— â— â— â— â—

Î¦95 Â Â Â Â â— â— â— â— â— â— â— â— â— â—

Î¦102 Â Â Â Â â— â— â— â— â— â— â— â— â— â—

Î¦108 Â Â Â Â â— â— â— â— â— â— â— â— â— â—

Î¦114 Â Â Â Â Â â— â— â— â— â— â— â— â— â—

Î¦121 Â Â Â Â Â â— â— â— â— â— â— â— â— â—

Î¦127 Â Â Â Â Â â— â— â— â— â— â— â— â— â—

Î¦133 Â Â Â Â Â â— â— â— â— â— â— â— â— â—

Î¦140 Â Â Â Â Â Â â— â— â— â— â— â— â— â—

Î¦146 Â Â Â Â Â Â â— â— â— â— â— â— â— â—

Î¦152 Â Â Â Â Â Â â— â— â— â— â— â— â— â—

Î¦159 Â Â Â Â Â Â â— â— â— â— â— â— â— â—

Î¦168 Â Â Â Â Â Â â— â— â— â— â— â— â— â—

Â

Hardfacing Elbow

At present, the elbow flowmeter produced by many manufacturers of elbow flowmeters is a 90-degree elbow with a standard geometry, and the construction party installing the throttling element often directly installs the elbow directly in a suitable space, but The effect of flow measurement is not very satisfactory.

Composite Overlay Elbows are suitable for extremely severe abrasive wear and moderate to low impact.

Weld overlay cladding is a process that provides protection for metallic components by welding a layer of abrasion-resistant alloy to areas at risk of wear. It can be applied to an entire component, or only to specific areas of concern. Typical components clad by HP Welding include pipes, valves, flanges, connectors, and elbows, as well as more complex geometries such as tee pieces and wye pieces.

Typical materials for cladding in common use at HP Welding include HP700, HP700S, HP750X, HP750P and stainless steels, as well as many less common alloys.

With over 30 years of experience on the production of hardfacing products, and the technical expertise to back them up, HP Welding can meet any base material and cladding combination.

The advantages of HP Hardfacing Elbows

1. Flat surface and nice appearance

2. Good weldability to others working pieces

3. Excellent wear resistance

HP Hardfacing Elbows can be widely applied to mining site, cement plant, metallurgical equipment, dredging and power generation and any other fields where need to combat with abrasion.

Hardfacing Elbow,Wear Resistant Tube Bends,Hardfacing Wear Pipe-Elbow,Chromium Carbide Overlay Pipe
HuiFeng Wear Resistant Group , https://www.hpwearsolution.com